ABSTRACT
The main degradations of paint coatings applied on substrates commonly used in the building sector or in civil engineering are presented in this article: masonry and exterior coatings, wood and woody materials as well as the principal metallic materials used in construction. The degradations and defects in coatings occurring after several years of exposure are listed in this article with indications on the possible causes for such degradations. The understanding of paint degradation requires sound knowledge of the support substrate; certain phenomena frequently occur on the same type of materials.
Read this article from a comprehensive knowledge base, updated and supplemented with articles reviewed by scientific committees.
Read the articleAUTHOR
-
Thierry LUCAS: Former director of ONHGPI (now OHGPI) and former chairman of the AFNOR T30A commission
INTRODUCTION
he purpose of this dossier is to present the main types of deterioration in paint coatings applied to substrates commonly encountered in building and civil engineering: masonry and exterior coatings, wood and wood materials, and the main metal construction materials. It covers the deterioration and defects that occur in coatings after a few years' exposure. In most cases, it gives indications of possible causes of deterioration.
However, it is not the purpose of this dossier to describe initial problems and pathologies that appear during paint application or in the hours that follow. In fact, anomalies of this type are dealt with in the "Protection and decoration by paint" file. . It should be noted that such anomalies can generally be dealt with by personnel qualified in the use of application equipment (e.g. certified operators) or, in the case of product preparation precautions, substrate condition or atmospheric conditions, by a suitably qualified operator (see § 1.4.2 Certification of paint systems and operators).
Nor is it the purpose of this dossier to establish the precise causes of the various paint coating degradations. Indeed, for each case, establishing the precise causes requires the expertise of competent controllers or inspectors, who will be informed of the details of the problem. In fact, degradations that appear to be equivalent, or even similar, may have their origins in quite different phenomena.
Why adopt a plan based on the main types of material used to support the paint coating?
The reason is quite simple. A coating of this kind generally has a thickness of less than one millimetre. Moreover, one of its main qualities is to be sufficiently adherent to its substrate (the substrate of the coating is preferably referred to as the "substrate"). It is therefore virtually automatic that defects in the substrate will be transmitted to the coating.
This is often the case for deformations in the substrate, such as cracks and living microcracks, which change width according to movement:
of thermal origin between hot and cold periods (case of masonry and concrete);
or due to variations in moisture content...
Exclusive to subscribers. 97% yet to be discovered!
You do not have access to this resource.
Click here to request your free trial access!
Already subscribed? Log in!
![](/assets/images/logo-eti-286623ed91fa802ce039246e516e5852.png)
The Ultimate Scientific and Technical Reference
CAN BE ALSO FOUND IN:
This article is included in
Formulation
This offer includes:
Knowledge Base
Updated and enriched with articles validated by our scientific committees
Services
A set of exclusive tools to complement the resources
Practical Path
Operational and didactic, to guarantee the acquisition of transversal skills
Doc & Quiz
Interactive articles with quizzes, for constructive reading
Paint degradation and durability
Bibliography
Standardization
Association française de normalisation AFNOR
1. General paint standards
- Peintures et vernis - Détermination de la réflexion spéculaire de feuils de peinture non métallisée à 20 degrés, 60 degrés et 85 degrés (indice de classement : T30-064). - NF EN ISO 2813 - 09.99
- Peintures et vernis - Comparaison visuelle...
Organizations
Association française de normalisation AFNOR http://www.afnor.org
Association pour la Certification et la Qualification en Peinture Anticorrosion ACQPA http://www.acqpa.com
Exclusive to subscribers. 97% yet to be discovered!
You do not have access to this resource.
Click here to request your free trial access!
Already subscribed? Log in!
![](/assets/images/logo-eti-286623ed91fa802ce039246e516e5852.png)
The Ultimate Scientific and Technical Reference